FusForceTM PET-CF is specially developed for FDM 3D printing process, and its substrate material is PET engineering plastic with low moisture absorption, high strength, creep resistance, excellent chemical resistance and high heat resistance. With good dimensional stability, no warpage and no shrinkage and no smell, no heating chamber are required during the printing process.
| Type | PET-GF (Red), PET-GF (Grey), PET-CF (Black) |
|---|
• Smart Fiber Reinforced Technology
FusRock® controlling the dispersion and distribution of chopped carbon fibers within the material
matrix during the extrusion process, the fibers form a mesh skeleton structure within the material
and bear most of the load transferred by the material matrix. Smart Fiber Reinforced Technology
greatly improves the mechanical properties and heat resistance of the material, and releases the
internal stress during the printing process through the fiber mesh structure, resulting in good
dimensional stability of the printed part and no warpage.
• Low creep
The molecular chain structure of PET is highly regular and has a rigid benzene ring structure, so
that PET has better mechanical properties and less deformation under long-term load.
Compared with PA and PC materials, PET has better creep-resistance.
Additional Suggestions：
1. Although the moisture absorption of PET material is very low, it is very sensitive to moisture.
Printing after absorbing moisture will result in ozzing, extruding with bubbles and rough surface
appearance, thus reducing print quality. It is recommended that put the filament into a dry box
(humidity below 15%) immediately after opening the FusForceTM PET-CF vacuum foil bag for
printing. Please put the unused filament back into the original aluminum foil bag for sealed
storage.
2. After the material is damp, there will be more printing ozzing, bubbles extruded and rough
printing surface. Please dry the filament in an oven at 100-120°C for 4-6h to restore the printing
quality of FusForceTM PET-CF.
3. Phaetus hardened steel and above grade nozzles shall be selected, which can effectively
improve the print quality. Besides, it is recommended that the thickness of the heating block
should no less than 12mm.
4. After the printing, the printed part can be annealed to further improve the strength of
FusForceTM PET-CF print part. Annealing conditions: place the printed part at 80-100 for 4-8
hours and cool to room temperature naturally.